Application LubriSilk®

LubriSilk Spray Lubricant (LSSP)

RTG Wire Rope Drum at Port.

LSSP removed all clogged, dried up existing grease. Sprayed with LSSP over the drum. Allowed it to set in for 5 minutes, used a dry cloth and wipe clean. The cleaning was done in 10 minutes. 

This is a pre-treatment process before greasing the drum with LubriSilk Grease #2 (LS18F)

RTG Metal Piece at Port.

Sprayed with LSSP over the metal piece. Allow it set in wet for 5 minutes, used a dry cloth and wiped clean. 80% of the corrosion was not visible. The metal piece looked moist.

Rusty pipe wrench.

Sprayed with LSSP on the wrench, on the 11th Nov . The wrench did not corrode when checked, 25th Nov 2017.  After a month still no visible rust.

LubriSilk Spray Lubricant (LSSP) 
LubriSilk Paint on Lubricant (LSPOL)

Rusty Main Gate

Sprayed with LSSP and left to set in for 20 minutes. Wiped clean with the dry cloth and repeated again. After which, paint it on with LSPOL.  No more formation of any rust.

LubriSilk Grease #2 (LS18F)

Foundry Conveyor Chain Analysis

Before 123802 ppm of iron.
Run Time 12/3/06 to 01/13/07.
2 washer Trial Run.

Grease fitting installed, after there was no damage to the bearing.

BCB lubrication provided protection under severe iron contamination.

LubriSilk Marine Grease #3 (LM18F)

Corrosion tests of steel prepared with Boron-CLS-Bond® Grease#3 and exposure in an aggressive environment

The corrosion test method is designed as following:
Untreated steel plates are exposed to a 8% NaCl solution for 4 weeks. After the test period the treated and untreated steel sample was analysed.
Result: All samples of unprepared steel samples showed significant corrosion already after a few hours.
The samples that were prepared with Boron CLS Bond® ingredient. In the test grease 18F, under water with a water wash out of 1.9%, showed no tendency of corrosion. After 4 weeks exposure, still no indication of corrosion.
(See picture, 1000 x magnification).
Test were conducted by Micromy AB, Hägernäs, Sweden. Tests commissioned by Tribolator AB.

LubriSilk® Firearms Lubricant, Cleaner and Metal Sealer (FLCMS)

Rizzini 28 Ga. Over/Under Smoothbore Shotgun

After firing approx. 125 rounds of Winchester Super X lead #5 shot per barrel, both barrels were sprayed with Crud Cutter solvent and brushed with a brass bore brush. Both barrels were then clean dry swabbed and then sprayed with Rem Oil and clean swabbed again. The firearm was then returned to the firearm safe.

Top Barrel:

After 48 days, the top barrel was swabbed. A clean swab forced through barrel to pick up any residual GSR from barrel.

Only a slight amount was recovered.

The following day, LubriSilk® FCLMS was sprayed into barrel. A clean swab forced through barrel to pick up any residual GSR from barrel.

A large amount of GSR was recovered.

Bottom Barrel:

After 48 days, the top barrel was swabbed. A clean swab forced through barrel to pick up any residual GSR from barrel.

Only a slight amount was recovered.

The following day, LubriSilk® FCLMS was sprayed into barrel. A clean swab forced through barrel to pick up any residual GSR from barrel.

A large amount of GSR was recovered.